MoSi2 Heating Elements / Molybdenum Heating Elements for Disilicide Furnace AIA-1 manufacturer from China Hubei Fotma Machinery Co., Ltd.

MoSi2 Heating Elements / Molybdenum Heating Elements for Disilicide Furnace

Place of Origin:

Guangdong, China (Mainland)


	Add to My Favorites
HiSupplier Escrow	Share \|

Product Detail

Model No.: AIA-1

MoSi2 Molybdenum Products Molybdenum Heating Elements for Disilicide Furnace Product Description Mo

MoSi2 Molybdenum Products Molybdenum Heating Elements for Disilicide Furnace

Product Description

MoSi2 heating elements is made from Molybdenum Disilicide with excellent thermal resistance. It can be used in air and various gases environments. Working temperature of MoSi2 heating element is 1300C to 1800C and it has been widely used as heaters in high temperature furnaces and kilns of metallurgy, glass, ceramic refractory, crystal electronic device, industrial furnace manufacture and chemical industry field.

Types of MoSi2 Heating Elements
1. According to temperature: 1700C and 1800C
2. According to Shape: U, W, I, UL, WL, Spiral types.

MoSi2 Heating Elements Standard Size:
(Hot zone dia / Cold zone dia)
3/6mm, 4/9mm, 6/12mm, 9/18mm, 12/24mm.

Chemical property of MoSi2
High temperature oxidation resistance:
When MoSi2 heating elements are used at high temperature and under oxidation circumstance, a dense layer of quartz (SiO2) is generated on the surface of the element to prevent it from further oxidation.
When the temperature of element is over 1700ºC, the SiO2 protecting film whose melting point is 1710ºC will be melted. Due to its surface tension, SiO2 agglomerate() into drops and lose protection. The SiO2 protecting film is formed again when the element continues to be used under the oxidation circumstance.
It must be pointed out is that the MoSi2 heating element cannot be used in the temperature between 400ºC to 700 ºC for long time. Otherwise, the element will be pulverized because of the strong low-temperature oxidation.

Resistance characters

MoSi2 heating elements have good resistance characteristic, so it is an ideal heating material to replace traditional heating elements.

At room temperature, its resistivity is very low, with the increase of temperature, the resistance increases sharply. The advantages of heating up fast and low power consumption are obvious.

In normal operating circumstances, the resistance of the element is constant, so the old and new components can be mixed.

Molybdenum MoSi2 Heating Elements' Application:

Item	Name	Distinction criterion	Specification	Using range
Heating elements	1700 type	Element operating temperature 1700ºC is acceptable	Le Φ 6-12W type/U type/L type/all kinds of hetero type / stripe shape	high temperature electric resistance furnace
	1800 type	Element operating temperature 1800ºC is acceptable		high temperature electric resistance furnace
	1800J type	Element operating temperature≥1800ºC	Le Φ 3-12W type	Special,high temperature and high-power electric resistance furnace
	1800T type	Element operating temperature≤1800ºC	Le Φ 3-12W type U type	Not oxidized special air high temperature electric resistance furnace

Atmosphere influence on the MoSi2 heater's operating temperature:

Atmosphere	The max element temperature(ºC)
	1700type	1800type
Air	1700	1800
N₂	1600	1700
He Ar Ne Argon, Helium	1600	1700
Dry Hydrogen(dew point) -80ºC	1150	1150
Wet Hydrogen(Dew point) -20ºC	1450	1450
mixed gas(e . g . 10%CO₂, 50%CO, 15% H₂)	1600	1700
mixed gas(e . g . 40%CO2 , 20%CO)	1400	1450
Cracked and partly burnt ammonia	1400	1450

Physics Characters of MoSi2

Bulk density	Bending strength	Hardness	Apparent porosity	Drawing water rate	Thermal elongation rate
5.6~5.8g/cm3	20MPa(20ºC)	(hv)570kg/mm²	0.5~2.0%	0.5%	4%